Steel components (such as sheets or wires) are galvanized using an automated process before they are cut to size. This automated process will vary depending on the type of galvanized part. In general, steel components are immersed in a "galvanizing bath" of molten zinc for a short period of time. After the steel is removed from the bath, excess zinc is removed using a mechanical wiper, air knife, or steam. This leaves a relatively thin layer of galvanizing.
Product Parameters
| Product Name | Prepainted Galvanized Steel Sheet |
| Thickness | 0.12mm-6.00mm |
| Width | 600mm-1500mm |
| Length | 1m-12m, Support Customization |
| Standard | AISI, ASTM, DIN, JIS, GB, JIS, SUS, EN, etc. |
| Zinc Layer | Hot Galvanizing: 60-275g/m² |
| Pre-galvanized: 80-275g/m² |
Chemical Composition
| Standard | Grade | C | Si | Mn | P | S | Ti |
| Forcold FormingChinese Standard | DX51D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX52D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX53D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX54D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX56D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| DX57D+Z | 0.12 | 0.50 | 0.60 | 0.100 | 0.045 | 0.30 |
| Forcold FormingJapanese Standard | SGCC | 0.15 | 0.50 | 0.80 | 0.050 | 0.030 | 0.025 |
SGCD1
SGCD2 | 0.12
0.10 | 0.50
0.50 | 0.60
0.45 | 0.040
0.030 | 0.030
0.030 | 0.025
0.025 |
| SGCD3 | 0.08 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| SGCD4 | 0.06 | 0.50 | 0.45 | 0.030 | 0.030 | 0.025 |
| For StructureJapanese Standard | SGC340 | 0.25 | 0.50 | 1.70 | 0.200 | 0.035 | 0.025 |
SGC400
SGC440 | 0.25
0.25 | 0.50
0.50 | 1.70
2.00 | 0.200
0.200 | 0.035
0.035 | 0.150
0.150 |
| SGC490 | 0.30 | 0.50 | 2.00 | 0.200 | 0.035 | 0.025 |
| SGC510 | 0.30 | 0.50 | 2.50 | 0.200 | 0.035 | 0.025 |
| For StructureAISI Standard | S220GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S250GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S280GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S320GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.025 |
| S350GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
| S550GD+Z | 0.20 | 0.60 | 0.70 | 0.100 | 0.045 | 0.150 |
Mechanical Properties
| Grade | Yield Strength MPa≥ | Tensile Strength MPa≥ | Elongation A%≥ |
| DX51D Z/ZM/AZ/AM | 240-380 | 270-500 | 22 |
| DX52D Z/ZM/AZ/AM | 140-300 | 270-420 | 26 |
| DX53D Z/ZM/AZ/AM | 140-260 | 270-380 | 30 |
| DX54D Z/ZM/AZ/AM | 120-220 | 260-350 | 36 |
| S220GD Z/ZM/AM | 220 | 300 | 20 |
| S250GD Z/ZM/AZ/AM | 250 | 330 | 19 |
| S280GD Z/ZM/AM | 280 | 360 | 18 |
| S300GD A/AM | 300 | 380 | 18 |
| S320GD Z/ZM/AM | 320 | 390 | 17 |
| S350GD Z/ZM/AZ/AM | 350 | 420 | 16 |
| S450GD A/AM | 450 | 480 | 15 |
| S550GD Z/ZM/AZ/AM | 550 | 550 | - |
Galvanized Surface Selection
| Zero Spangle | Minimized Spangle | Normal Spangle | Large Spangle |